Decay resistance, physical, mechanical, and thermal properties of heated oriental beech wood
Yükleniyor...
Dosyalar
Tarih
2015
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Statny Drevarsky Vyskumny Ustav
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Heat treatment of Oriental beech (Fagus orientalis) wood was carried out by hot air in an oven for 2, 6, and 10 h at 125, 155, and 185°C. After heat treatment; decay resistance, oven dry density, modulus of rupture (MOR), compression strength parallel to grain (CSPG), and thermal characteristics of Oriental beech wood were investigated. Our results showed that heat treatment caused a decrease in oven dry density values of Oriental beech wood specimens. Heat treatment improved decay resistance of Oriental beech wood. Moreover, higher temperature and durations resulted in lower mass loss of wood after decay test. MOR values of heated Oriental beech decreased with increasing temperature and durations. CSPG values of Oriental beech decreased after heat treatments except for 2 and 6 hours heating at 125°C. According to the thermal analysis results, thermal properties of heated Oriental beech wood were preserved except for heated Oriental beech wood at 185°C for 6 and 10 hours.
Açıklama
Anahtar Kelimeler
CSPG, Decay resistance, Heat Treatment, MOR, Oriental Beech, Oven Dry Density, Thermal Characteristics
Kaynak
Wood Research
WoS Q Değeri
N/A
Scopus Q Değeri
Q2
Cilt
60
Sayı
6