Microstructure characterization and hardness of Al-Cu-Mn eutectic alloy
Yükleniyor...
Tarih
2018
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Foundry Journal Agency
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
The composition of Al-Cu-Mn ternary eutectic alloy was chosen to be Al-32.5wt.%Cu-0.6wt.%Mn to the Al2Cu and Al12CuMn2 solid phases within an aluminum matrix (alpha-AI)from its melt. The Al-32.5wt.%Cu-0.6wt.%Mn alloy was directionally solidified at a constant temperature gradient (8.1 K.mm(-1)) with different growth rates, 8.4 to 166.2 mu m.s(-1) , by using a Bridgman-type furnace. The eutectic temperature (the melting point) of 547.85 degrees C for the AI-32.5wt.%Cu-0.6wt.%Mn alloy was obtained from the DTA curve of the temperature difference between the test sample and the inert reference sample versus temperature or time. The lamellar spacings (lambda) were measured from transverse sections of the samples. The dependencies of lamellar spacings (lambda(Al-A12Cu)) and microhardness on growth rates were obtained as, lambda(Al-A12Cu)=3.02V(-0.36) , HV=153.2(V)(0)(.0)(35) , HV=170.6(lambda)(-0.09) and HV=144.3+0.82(lambda(Al-A12Cu))(-0.50), HV=149.9+53.48V(0.25) , respectively, for the Al-Cu-Mn eutectic alloy. The bulk growth rates were determined as lambda(2)(Al-A12Cu).V= 25.38 mu m(3).s(-1) by using the measured values of lambda(Al-A12Cu) and V. A comparison of present results was also made with the previous similar experimental results.
Açıklama
Anahtar Kelimeler
Directional Solidification, Aluminum Alloys, Microstructure, Hardness Test
Kaynak
China Foundry
WoS Q Değeri
N/A
Scopus Q Değeri
Q2
Cilt
15
Sayı
5