    Review on ballistic tribology
    (2004) Cerit, Afşın Alper; Karamış, Baki M.; Nair, Fehmi
    In this paper, it was investigated that studies about the dynamic failure of reinforced metal matrix composites and fiber composites under high velocity impact was observed. Some of this works on this topic is experimental, and they used normal projectile or Armour piercing projectile in ballistic tests. The other works in ballistic system are computer simulations. They use finite element based program for numerical investigation. According to the studies, high velocity of projectile led to the melting of some surface layers because of the excess heat resulting from high velocity friction. However different failure mechanisms such as radial cracking, melting zones, etc. were earlier determined. In some simulation this results had been supported.
  • Küçük Resim
    Öğe
    Tel haddeleme tekniği ile Cu/Mgb2 süper iletken tellerin üretimi ve üretim parametrelerinin ürün özelliklerine etkilerinin incelenmesi
    (TÜBİTAK MAG Proje, 2015) Cengil, Mehmet; Nair, Fehmi; Karabörk, Fazliye
    Bu projede, tüp içerisinde toz (Powder in Tube, PIT) yöntemi ile hazırlanmış Cu/MgB2 kompozit yapıların, tel haddeleme tekniği kullanılarak süper iletken tellere dönüştürülmesi ve üretim parametrelerinin ürün özelliklerine etkisi araştırılmıştır. Bu amaçla, farklı çaplarda (min. 0.55 mm) tek ve çok özlü teller, bariyer malzemesi kullanılmadan ve kullanılarak üretilmiştir. Farklı geometrilerdeki bu tellerin üretimi, bakır tüp içerisine açılan deliğe MgB2 tozlarının doldurulmasıyla hazırlanan kompozit biletlerin ekstrüzyonuyla üretilen filmaşinler veya doğrudan bu kompozit biletler kullanılarak, haddeleme işlemi ile yapılmıştır. Haddeleme öncesi üretim aşamalarında, malzmenin plastik deformasyon kabiliyetinin arttırılması ve ürün özelliklerinin bozulmaması için, gerek görülen durumlarda ara tavlamalar yapılmıştır.
  • Küçük Resim
    Öğe
    The effects of different ceramics size and volume fraction on wear behavior of Al matrix composites (for automobile cam material)
    (Elsevier, 2012) Karamış, Mehmet Baki; Cerit, Afşin Alper; Selçuk, Burhan; Nair, Fehmi
    In this study, a number of metal matrix composites were manufactured to determine their tribological properties. AA2124 matrix material, reinforced by SiC, B 4C or Al 2O 3 (of different particle sizes), was used for manufacturing by powder metallurgy. The reinforcing particles were included at 10%, 20% and 30% volume fraction (vf). The matrix and reinforcement powders were compressed at 600MPa and 615°C for 30min in an argon atmosphere. For comparison with the metal matrix composites (MMC), unreinforced AA2124 samples and GGG40 cam material samples (both induction-hardened and untreated) were also prepared for tribological tests. Tribological tests were conducted at 50N loading with 900rpm revolution for 30min under dry conditions. The specific wear rates of the composites reinforced with 10% volume fraction of B 4C or SiC are each lower than that of the GGG40 cam material. While the composite having 30% volume fraction of 20?m SiC gives the best wear performance, the sample with B 4C shows the best performance at 10% vf.